• Composite Type: Micro Hybrid
• Cure Type: Light Cure
• Shade: A1,A2,A3,B2
• Polymerization Shrinkage: 3.1%
• Young's Modulus (Mpa): 11,173
• Bending Strength (Mpa): 157
• Vicekr Hardness (Mpa): 784
• Compressive Strength (Mpa): 502
• Filler Load: 75% Per Volume
• Filler Size: 0.04-3.0 Microns
• Tesile Strength (Mpa): 50

Storage:

• Store in a cool and dry place
• Store at room temperature of 5-30 degree C
• Store away from direct sunlight.

• 1 x 4g Syringe

• Preparation: Begin by thoroughly preparing the tooth for restoration, ensuring proper cleaning and isolation for an optimal working environment.
• Shade Selection: Choose the suitable shade of Restorite Micro Hybrid Composite that closely matches the natural color of the tooth for seamless integration.
• Etching and Bonding: Apply an appropriate dental etching gel to the prepared tooth surface, followed by the application of a compatible bonding agent. Adhere to recommended guidelines for these products.
• Material Dispensing: Extrude the Restorite Micro Hybrid Composite material onto the prepared tooth structure using a syringe or capsule, distributing it as needed.
• Sculpting and Contouring: Use suitable composite instruments to sculpt and contour the material to achieve the desired shape and anatomical features before the material sets.
• Curing: Employ a dental curing light to light-cure the Restorite Micro Hybrid Composite material. Ensure compliance with the recommended curing time.
• Finishing and Polishing: After complete curing, proceed with finishing and polishing steps to attain a smooth and aesthetically pleasing surface. Utilize appropriate instruments for polishing.
• Occlusal Adjustment: Verify and adjust occlusion as needed to ensure proper alignment and functional bite. Make necessary adjustments for optimal results.
• Post-Operative Instructions: Provide the patient with post-operative care instructions, including information on potential sensitivity and proper oral hygiene practices.
  • Final Assessment: Conduct a comprehensive final assessment of the restoration, considering both functional and aesthetic aspects.