Physical properties:

• Polymerization Shrinkage: 2.8%
• 3-Point-Strength (Mpa): 144
• Young’s Modulus (Mpa): 12,316
• Vickers Hardness (Mpa): 794
• Compressive Strength (Mpa): 431
• Radiopacity : 210% AI
• Filler Content: 77% by weight%

Storage:

• Store all kit contents away from sunlight in a cool and dry place. Refrigerate material, do not freeze.

• 4 x 2gm Syringe (A1,A2,A3,B2)
• 20 x Application Needles For Restorite Bulk Fill

• Pretreatment: Before commencing the treatment, clean the tooth with a non-fluoride polishing paste (Prime Dental's Aster Prophy). Use a Vita® shade guide to select the shade while the tooth is still moist.
• Cavity preparation: Minimal-invasive preparation of the cavity as generally required for adhesive techniques. All enamel margins in the anterior region must be beveled. Do not bevel the margins in the posterior region and avoid slice preparations. Spray the cavity with water to clean it, remove all debris, and dry it. The cavity must be isolated. It is advisable to place a rubber dam.
• Pulp protection/ Cavity liner: If an enamel-dentine adhesive is used during regular cavities no cavity liner is required. In very deep cavities areas in close proximity to the pulp must be coated with a calcium hydroxide material. (Prime Dental's Restorite LC Cal)
• Approximal Contact Areas: When filling cavities with approximal sections, place a transparent matrix and fix it in place.
• Bond: Take Restorite Bond 7G Self Cure Unscrew the cap. Squeeze out the exact number of drops you need into the disposable well. When finished, screw the cap back onto the bottle. Immediately after dispensing apply 2-3 consecutive coats of adhesive to enamel and dentine for 15 seconds with gentle agitation using a fully saturated applicator. Gently air thin for five seconds to evaporate solvents. Light cure for 10 seconds.
• Composite Filling: Dispense Restorite Flow Viscous in thin layers (max. 2mm) directly into the cavity. Use the black hub disposable curved application tips included with the kit. For hygiene reasons, do not use the application tips more than one time. Avoid introducing air bubbles into the material during application with the tip. Due to the effect of the oxygen in the air, a thin layer of unpolymerized material remains on the surface of each layer. This bonds the layers chemically and should not be touched or contaminated with moisture.
• Curing: All shades must be light-cured for 40 seconds per layer using a commercially available light-curing unit. The light guide must be held as close as possible to the surface of the filling. Multiple surface fillings should be light-cured from each side.
• Trimming: Restorite Flow Viscous Composite can be trimmed and polished immediately after curing using finishing diamonds, flexible disks, silicone polishers, and polishing brushes. Check the occlusion articulation and spot grind to eliminate high spots or undesirable paths of articulation from the surface of the filling.
• Final Finish: Apply Aster Compo paste on the cup/brush or directly over the tooth or on the restoration material. Use the paste in low rotation, applying low pressure with intermittent touches and in circular movements. The paste is thixotropic in nature and more fluidity can be attained when subjected to rotation. After the final finishing use Prime Dental's Restorite Cavo Surface Sealer. It is a light-cured unfilled methacrylate resin that penetrates, seals cracks and surface porosity in composite restorations. This product applied at the restoration placement and on an annual basis, improves marginal integrity of composite restorations by filling microscopic cracks in composite surfaces.