• Flexural modulus - 9000 MPa
• Flexural strength - 127 MPa
• Water sorption - 16µg/mm3
• Water solubility - 0.9µg/mm3
• Radiopacity - 2 mm Al
• Vickers hardness - 73 kg/mm2
• Volumetric shrinkage - 2.1%
• Compressive strength - 392 MPa
• Minimum filler particle size - 20 nm
• Average filler particle size - 0.6μm
• Filler content by weight - 80%
• Filler content by volume - 65%
• Density - 2.0 g/cm3

1 X 4gm Syringe

Preparation:

• Prepare the tooth surface according to standard dental procedures.

Mixing:

• Mix the material thoroughly according to the provided instructions, ensuring a homogenous blend.

Application:

• Apply the material with firm consistency, sculpting as needed for the desired contour and shape.

Curing:

• Use an operatory light for the recommended duration to facilitate proper polymerization.

Finishing:

• Quickly polish the cured material for a smooth and esthetic finish.

Quality Check:

• Verify the shade match, contour, and overall appearance.

Radiographic Confirmation:

• Confirm radiopacity through X-rays if necessary, ensuring proper visibility.

Post-Application Instructions:

• Provide post-application care instructions to the patient.

Record Keeping:

• Maintain detailed records of the procedure and material used for future reference.