Formulation: The resin based matrix contains approximately 19 wt% of Bis-GMA based dimethacrylate system. The filler system contains approximately 80 wt% (65vol%) silanated 40 nanometer ytterbium fluoride, silanated 500 nanometer barium glass and 10 nanometer silica. Thereis approximately 1wt% of catalyst, inhibitors and pigment.

• Compressive Strength : 295 MPa
• Flexural Strength : 127 MPa
• Flexural Modulus : 10,800 MPa
• Tensile Strength : 58 MPa
• Water absorption : 5pg/mm3
• Solubility : 25pg/mm

• 1 x 4g syringe

• Isolation: Isolate the tooth from saliva and moisture using a dental dam or appropriate methods.
• Cleaning: Thoroughly clean the cavity, removing debris, decay, and contaminants.
• Bonding: Apply a suitable dental bonding system or adhesive to the cavity walls as instructed for application and curing.
• Composite Placement: Dispense a small amount of resin composite and adapt it into the cavity, ensuring proper adaptation to the walls and contours of the tooth.
• Contouring and Shaping: Use dental instruments to contour and shape the composite material to achieve the desired anatomical form and occlusion.
• Finishing and Polishing: After curing, use suitable finishing and polishing techniques (e.g., burs, discs, polishing pastes) to achieve a smooth and esthetic surface.